Santoprene™ TPV 101-73
>TPV<
阻燃等级: HB
邵氏硬度A: 78
压缩形变: 27 %
加工方式: 注射成型 挤出成型 吹塑成型 热成型 真空成型
材料属性: 板材级 型材级
符合规定: UL UL-746C F1 UL-749 F3 UL-2157F4
材料特性: 抗蠕变 绝缘 耐疲劳 尺寸稳定 可回收材料 良好的电气性能 耐热老化 压缩形变低 耐臭氧 耐化学性
材料用途: 电气元件 家电部件 汽车领域的应用 汽车引擎盖 消费品应用 隔
规格级别耐化学性良好,耐臭氧性能,良好的电气性能,可回收材料,耐疲劳性能,良好的抗蠕变性,低的压缩变形性,绝缘,尺寸稳定性良好,良好的耐热老化性能真空成型,共挤出成型,片材挤出成型,多次注射成型,吹塑成型,挤出吹塑成型,热成型,注射成型,型材挤出成型,注吹成型,挤出外观颜色黑色该料用途汽车领域的应用,密封件,管件,家电部件,消费品应用领域,汽车的发动机罩下的零件,室外应用,垫圈,电气元件,隔膜备注说明加工条件:真空成型,共挤出成型,片材挤出成型,多次注射成型,吹塑成型,挤出吹塑成型,热成型,注射成型,型材挤出成型,注吹成型,挤出。技术参数
性能项目试验条件[状态]测试方法测试数据数据单位物理性能比重ASTMD7920.968g/cm³密度
ISO11830.970g/cm³室外适用性
UL746Cf1
DetergentResistance
UL2157f4
UL749f3
ELASTOMERS弹性体
TestMethodNominalValueUnit拉伸应力-横向流量(应变,23°C)
ASTMD4123.60MPa
ISO373.60MPa抗张强度-横向流量(断裂,23°C)
ASTMD4128.80MPaTensileStress-AcrossFlow(Break,23°C)
ISO378.80MPa伸长率-横向流量(断裂,23°C)
ASTMD412490%
ISO37490%撕裂强度-横向流量2(23°C)
ASTMD62427.0kN/mTearStrength-AcrossFlow3(23°C)
ISO34-127kN/mCompressionSet470°C,22hrASTMD395B28%125°C,70hrASTMD395B37%压缩变形470°C,22hrISO81528%125°C,70hrISO81537%硬度肖氏硬度(邵氏A,15秒,23°C)
ISO86878
热性能脆化温度
ASTMD746-60.0°C
ISO812-60.0°CRTIElec
UL74690.0°CRTIStr1.0mmUL74690.0°C1.5mmUL74690.0°C3.0mmUL74695.0°C老化空气中拉伸强度的变化率(150°C,168hr)
ASTMD573-1.0%
ISO188-1.0%空气中极限伸长率的变化率(150°C,168hr)
ASTMD573-3.0%ChangeinTensileStrainatBreakinAir(150°C,168hr)
ISO188-3.0%ChangeinDurometerHardnessinAir(ShoreA,150°C,168hr)
ASTMD5737.0
ChangeinShoreHardnessinAir(ShoreA,150°C,168hr)
ISO1887.0
拉伸强度的变化率23°C,168hr,inAceticAcidASTMD471-8.0%23°C,168hr,inCyclohexaneASTMD47131%23°C,168hr,inDetergent(Tide),2.5%ASTMD4713.0%23°C,168hr,inEthanol,95%ASTMD471-2.0%23°C,168hr,inHydrochloricAcid,10%ASTMD47113%23°C,168hr,inIsopropylAlcoholASTMD47131%23°C,168hr,inMethylethylketoneASTMD47147%23°C,168hr,inSodiumChloride,15%ASTMD4710.0%23°C,168hr,inSodiumHydroxide,50%ASTMD4713.0%23°C,168hr,inSulfuricAcid,98%ASTMD471-17%23°C,168hr,inTrichloroethyleneASTMD47154%100°C,168hr,inDeionizedWaterASTMD4711.0%100°C,168hr,inIRM903OilASTMD471-30%125°C,70hr,inIRM903OilASTMD471-31%125°C,168hr,inIRM903OilASTMD471-31%23°C,168hr,inAceticAcidISO1817-8.0%23°C,168hr,inCyclohexaneISO181731%23°C,168hr,inDetergent(Tide),2.5%ISO18173.0%23°C,168hr,inEthanol,95%ISO1817-2.0%23°C,168hr,inHydrochloricAcid,10%ISO181713%23°C,168hr,inIsopropylAlcoholISO181731%23°C,168hr,inMethylethylketoneISO181747%23°C,168hr,inSodiumChloride,15%ISO18170.0%23°C,168hr,inSodiumHydroxide,50%ISO18173.0%23°C,168hr,inSulfuricAcid,98%ISO1817-17%23°C,168hr,inTrichloroethyleneISO181754%100°C,168hr,inDeionizedWaterISO18171.0%100°C,168hr,inIRM903OilISO1817-30%125°C,70hr,inIRM903OilISO1817-31%125°C,168hr,inIRM903OilISO1817-31%极限伸长率的变化率23°C,168hr,inAceticAcidASTMD471-4.0%23°C,168hr,inCyclohexaneASTMD47120%23°C,168hr,inDetergent(Tide),2.5%ASTMD4712.0%23°C,168hr,inEthanol,95%ASTMD4710.0%23°C,168hr,inHydrochloricAcid,10%ASTMD4719.0%23°C,168hr,inIsopropylAlcoholASTMD47120%23°C,168hr,inMethylethylketoneASTMD47124%23°C,168hr,inSodiumChloride,15%ASTMD471-2.0%23°C,168hr,inSodiumHydroxide,50%ASTMD4712.0%23°C,168hr,inSulfuricAcid,98%ASTMD471-27%23°C,168hr,inTrichloroethyleneASTMD47122%100°C,168hr,inDeionizedWaterASTMD471-7.0%100°C,168hr,inIRM903OilASTMD471-49%125°C,70hr,inIRM903OilASTMD471-47%125°C,168hr,inIRM903OilASTMD471-58%断裂时拉伸应力变化23°C,168hr,inAceticAcidISO1817-4.0%23°C,168hr,inCyclohexaneISO181720%23°C,168hr,inDetergent(Tide),2.5%ISO18172.0%23°C,168hr,inEthanol,95%ISO18170.0%23°C,168hr,inHydrochloricAcid,10%ISO18179.0%23°C,168hr,inIsopropylAlcoholISO181720%23°C,168hr,inMethylethylketoneISO181724%23°C,168hr,inSodiumChloride,15%ISO1817-2.0%23°C,168hr,inSodiumHydroxide,50%ISO18172.0%23°C,168hr,inSulfuricAcid,98%ISO1817-27%23°C,168hr,inTrichloroethyleneISO181722%100°C,168hr,inDeionizedWaterISO1817-7.0%100°C,168hr,inIRM903OilISO1817-49%125°C,70hr,inIRM903OilISO1817-47%125°C,168hr,inIRM903OilISO1817-58%硬度计硬度的变化率2ShoreA,23°C,168hr,inAceticAcidASTMD471-2.0
ShoreA,23°C,168hr,inCyclohexaneASTMD471-16
ShoreA,23°C,168hr,inDetergent(Tide),2.5%ASTMD4710.0
ShoreA,23°C,168hr,inEthanol,95%ASTMD4710.0
ShoreA,23°C,168hr,inHydrochloricAcid,10%ASTMD471-3.0
ShoreA,23°C,168hr,inIsopropylAlcoholASTMD471-1.0
ShoreA,23°C,168hr,inMethylethylketoneASTMD4710.0
ShoreA,23°C,168hr,inSodiumChloride,15%ASTMD4710.0
ShoreA,23°C,168hr,inSodiumHydroxide,50%ASTMD4710.0
ShoreA,23°C,168hr,inSulfuricAcid,98%ASTMD4710.0
ShoreA,23°C,168hr,inTrichloroethyleneASTMD471-3.0
ShoreA,100°C,168hr,inDeionizedWaterASTMD471-2.0
ShoreA,100°C,168hr,inIRM903OilASTMD471-21
ShoreA,125°C,168hr,inIRM903OilASTMD471-23
ChangeinShoreHardnessShoreA,23°C,168hr,inAceticAcidISO1817-2.0
ShoreA,23°C,168hr,inCyclohexaneISO1817-16
ShoreA,23°C,168hr,inDetergent(Tide),2.5%ISO18170.0
ShoreA,23°C,168hr,inEthanol,95%ISO18170.0
ShoreA,23°C,168hr,inHydrochloricAcid,10%ISO1817-3.0
ShoreA,23°C,168hr,inIsopropylAlcoholISO1817-1.0
ShoreA,23°C,168hr,inMethylethylketoneISO18170.0
ShoreA,23°C,168hr,inSodiumChloride,15%ISO18170.0
ShoreA,23°C,168hr,inSodiumHydroxide,50%ISO18170.0
ShoreA,23°C,168hr,inSulfuricAcid,98%ISO18170.0
ShoreA,23°C,168hr,inTrichloroethyleneISO1817-3.0
ShoreA,100°C,168hr,inDeionizedWaterISO1817-2.0
ShoreA,100°C,168hr,inIRM903OilISO1817-21
ShoreA,125°C,168hr,inIRM903OilISO1817-23
质量变化率23°C,168hr,inAceticAcidASTMD4714.0%23°C,168hr,inCyclohexaneASTMD471-4.9%23°C,168hr,inDetergent(Tide),2.5%ASTMD4710.60%23°C,168hr,inEthanol,95%ASTMD471-0.10%23°C,168hr,inHydrochloricAcid,10%ASTMD4710.20%23°C,168hr,inIsopropylAlcoholASTMD471-13%23°C,168hr,inMethylethylketoneASTMD471-24%23°C,168hr,inSodiumChloride,15%ASTMD4710.20%23°C,168hr,inSodiumHydroxide,50%ASTMD471-0.20%23°C,168hr,inSulfuricAcid,98%ASTMD4713.6%23°C,168hr,inTrichloroethyleneASTMD471-6.0%100°C,168hr,inDeionizedWaterASTMD4713.6%100°C,168hr,inIRM903OilASTMD47166%125°C,168hr,inIRM903OilASTMD47178%23.0°C,168hr,inMethylethylketoneISO1817-24%23.0°C,168hr,inIsopropylAlcoholISO1817-13%23.0°C,168hr,inTrichloroethyleneISO1817-6.0%23.0°C,168hr,inCyclohexaneISO1817-4.9%23.0°C,168hr,inSodiumHydroxide,50%ISO1817-0.20%23.0°C,168hr,inEthanol,95%ISO1817-0.10%23.0°C,168hr,inHydrochloricAcid,10%ISO18170.20%23.0°C,168hr,inSodiumChloride,15%ISO18170.20%23.0°C,168hr,inDetergent(Tide),2.5%ISO18170.60%23.0°C,168hr,inSulfuricAcid,98%ISO18173.6%100°C,168hr,inDeionizedWaterISO18173.6%23.0°C,168hr,inAceticAcidISO18174.0%100°C,168hr,inIRM903OilISO181766%125°C,168hr,inIRM903OilISO181778%体积变化(125°C,70hr,在IRM903油中)
ASTMD47172%
ISO181772%ContinuousUpperTemperatureResistance(1008hr)
SAEJ2236135°C电气性能DielectricStrength(23°C,2.00mm)
ASTMD14927kV/mmDielectricConstant(23°C,1.98mm)
ASTMD1502.50
IEC602502.50
相比耐漏电起痕指数(CTI)
UL746PLC0
高电弧燃烧指数(HAI)
UL746PLC0
高压电弧抗点燃指数(HVAR)(PLC)
UL746PLC6
高电压电弧起痕速率(HVTR)
UL746PLC1
热丝引燃(HWI)1.0mmUL746PLC4
1.5mmUL746PLC3
3.0mmUL746PLC3
可燃性UL阻燃等级1.0mmUL94HB
1.5mmUL94HB
3.0mmUL94HB