Elastollan TPU 1190A10
>TPU<
邵氏硬度A: 90
撕裂强度: 128 KN/m
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.13 | g/cm³ | |
| 熔流率（熔体流动速率） | 190°C/10.0kg | ASTMD1238 | 10to20 | g/10min | |
| 190°C/21.6kg | ASTMD1238 | 10to40 | g/10min | ||
| 机械性能 | 拉伸模量(注塑) | ASTMD412 | 31.0 | MPa | |
| 弯曲模量(注塑) | ASTMD790 | 29.0 | MPa | ||
| 泰伯耐磨性 | ASTMD1044 | 45.0 | mg | ||
| Abrasion-DIN | DIN53516 | 25 | mm³ | ||
| ELASTOMERS | 弹性体 | TestMethod | NominalValue | Unit | |
| 拉伸应力(应变) | ASTMD412 | 12.4 | MPa | ||
| 拉伸应力(300%应变) | ASTMD412 | 27.6 | MPa | ||
| 抗张强度 | ASTMD412 | 37.2 | MPa | ||
| 伸长率(断裂) | ASTMD412 | 460 | % | ||
| 撕裂强度2 | ASTMD624 | 128 | kN/m | ||
| 压缩变形 | 23°C,22hr | ASTMD395B | 25 | % | |
| 70°C,22hr | ASTMD395B | 45 | % | ||
| 硬度 | 肖氏硬度(邵氏A) | ASTMD2240 | 90 | ||
| 热性能 | 玻璃转化温度 | InternalMethod | -35.0 | °C | |
| 维卡软化温度 | ASTMD1525 | 120 | °C | ||
| SofteningPoint-DMA | InternalMethod | 100 | °C | ||